Overview
Binary copper alloy and aluminium with a 5 to the 11% of aluminium, that it can contain also Fe , Mn and Neither to form alloys complejas.Las characteristic of these alloys come determined by their/its/your/his microestructura, that it is feature of the typesetting and of the industrious thermal processing.
|
| DESIGNATION |
(Kg/mm²) |
Limit elastic (Kg/mm²) |
Stretching (%) |
Hardness Brinell (HB) |
Conductivi.. electrical (%I.A.C.S) |
| K-401 |
Cu Al 5 |
R
F |
38
45-53 |
15
30-45 |
55
25-15 |
85
115-140 |
15-18 |
| K-402 |
Cu Al 8 |
R
F |
42
50-57 |
17
35-43 |
45
20-15 |
90
130-150 |
13-15 |
| K-403 |
Cu al 8 Fe 3 |
|
52-55 |
27-28 |
35-30 |
130-150 |
12-14 |
| K-404 |
Cu Al 9 Mn 2 |
|
52-65 |
25-40 |
25-15 |
130-160 |
12-14 |
| K-405 |
Cu Al 10 Fe 3 |
|
62-70 |
32-45 |
18-10 |
160-180 |
12-14 |
| K-406 |
Cu Al 10 Fe 5 Ni 5 |
|
75-80 |
42-50 |
15-12 |
180-215 |
7-9 |
| K-407 |
Cu Al 9 Ni 6 Fe 3 |
|
60-65 |
32-50 |
15 |
160-200 |
7-9 |
| Applications, when is wanted to obtain a good: |
K-401 |
K-402 |
K-403 |
K-404 |
K-405 |
K-406 |
K-407 |
| Resistance to the corrosion |
XX |
XX |
XX |
XX |
XX |
XXX |
XXX |
| Resistance to the warm oxidation |
XXX |
XXX |
XXX |
XXX |
XXX |
XXX |
XXX |
| Tools |
A |
A |
A |
A |
XX |
XXX |
XX |
| Mechanical resistance |
X |
X |
XX |
XX |
XXX |
XXX |
XXX |
| Characteristic of friction |
X |
X |
X |
XX |
XXX |
XXX |
XXX |
| To solder |
XX |
XX |
XXX |
XX |
XXX |
XXX |
XXX |
| Decorative effect |
X |
XXX |
|
|
|
|
|
|
Approximate specific weight: 7,6 kg/dm³
R: Coved
F: Wrought
Other cuproaluminios special low demand
|
|
| Supply |
In molten pieces, wrought, stamped or laminated |
|
|
|
| |
| |
|
|
|